Aluminum 6061-T6; 6061-T651. Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal. Close Analogs: Bearing Yield Strength: 3 56000 psi Edge distance/pin diameter = 2.0: Poisson\'s Ratio: 0.33: 0.33 Estimated from trends in similar Al alloys. Fatigue Strength: 96.5
Aluminum 6061-T6 has a minimum yield strength of 35 ksi (240 MPa), which is almost equal to that of A36 steel. This strength, combined with its light weight (about 1/3 that of steel), makes it particularly suitable for structural applications where static loads are a
6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35
Tensile Yield Strength: 276 MPa: 40000 psi: AA: Typical: Elongation at Break: 12%: 12%: AA; Typical; 1/16 in. (1.6 mm) Thickness: Modulus of Elasticity: 68.9 Gpa: 10000 ksi: Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and excellent
Tensile and Yield Strength: Aluminum 6061-T6 provides high tensile strength (approximay 310 MPa) and yield strength (around 276 MPa), making it ideal for load-bearing applications. Fatigue Strength: This alloy has a fatigue strength of about 96.5 MPa for 500 million cycles. For applications involving repeated stress, such as in aerospace
6061 Aluminum Alloy: Properties General Characteristics Characteristic Appraisal Yield Strength 145 MPa | 21000 psi 276 MPa | 40000 psi Modulus of Elasticity Thermal Properties Property 6061-T4 6061-T6 Coefficient of Thermal Expansion 20.0 - 100 °C Temp 23.6 µm/m-°C | 13.1 µin/in-°F 23.6 µm/m-°C | 13.1 µin/in-°F Thermal
6061-T6 Alloy Aluminium Properties The below table outlines the material properties for 6061-T6 Alloy material including the young\'s modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical
Aluminum 6061-T6; 6061-T651 Categories: Metal; Nonferrous Metal; Aluminum Alloy; 6000 Series Aluminum Alloy Material Notes: Information provided by Alcoa, Starmet and the references. General 6061 characteristics and uses: Tensile Strength, Yield 276 MPa 40000 psi AA; Typical 12.0 MPa Temperature 371 °C 1740 psi Temperature 700 °F 0.2%
Learn important details about aluminum 6061 and other metals using the OnlineMetals Product Guide. ISO AlMg1SiCu, AA6061-T6, Al6061-T651, AA6061-T4, Al6061-T4. Specifications - Aluminum 6061 . Yield Tensile Strength: 8 Fatigue Strength: 9 Shear Strength: 12
Yield strength of 6061-0 aluminum is 55 MPa, yield strength of 6061-T4 aluminum is 145 MPa, yield strength of 6061-T6 aluminum is 275 MPa. For metal materials without obvious yield phenomenon, it is stipulated that the stress value that produces 0.2% residual deformation is used as its yield limit, which is called conditional yield limit or
General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers offer better chipping characteristics over the T6
Mechanical Properties Aluminium 6061-T6 mechanical properties are listed in the following tables including yield strength (yield stress), ultimate tensile strength, shear strength, modulus of elasticity, young\'s modulus, etc. The following mechanical properties is the average value of various sizes, product forms and manufacturing methods, so the properties cannot be guaranteed. They are
6061-T6 aluminium standard heat treating process T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [10] This
Two critical strength measures for 6061-T6 aluminum are yield strength and ultimate strength. The yield strength, which is the maximum stress the material can endure while remaining elastically deformed, is 276 MPa (40,000
The below table outlines the material properties for 6061-T6 Alloy material including the young\'s modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical
Overview Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and excellent mability, it is perfect for applications in aerospace, transportation equipment and construction materials manufacturing. Aluminum 6061-T6 is generally heat treated and artificially aged for maximum
6061 Aluminum Alloy: PropertiesGeneral
6061-t6 yield strength is the yield limit of the 6061 t6 aluminum material when the yield phenomenon occurs, that is, the stress that resists a small amount of plastic
Aluminum 6061-T6; 6061-T651 Applications: Aircraft fittings, camera lens mounts, couplings, marines fittings and hardware, electrical fittings and connectors, decorative or misc. hardware, hinge pins, magneto parts, brake pistons, hydraulic pistons, appliance fittings, valves and valve parts; bike
The 6061-T6 extruded aluminum alloy boasts impressive strength, comparable to many steels. It has a tensile strength of 45,000 psi (pounds per square inch) and a yield strength of 40,000 psi, making it suitable for structural